Superior Quality PU Foam Adhesive for EPS Polyurethane Bonding Spray Glue

• Customization: Available
• CAS No.: 230-391-5
• Formula: Mixture
• Model NO.: 7085-85-0
• EINECS: 230-391-5
• Bonding Function: Instant Adhesive
• Morphology: Solvent
• Application: Automobile, Construction, Woodworking, Footwear & Leather, Fiber & Garment, Packing
• Material: Polyurethane
• Classification: Adhesive
• Main Agent Composition: Polyurethane Elastomer
• Characteristic: Weatherability
• Promoter Composition: Curing Agent
• Composition: Organic Material
• Color: White
• Type: Bond
• Shelf Life: 12 Months
• Transport Package: Sea Shipping
• Specification: 750ml
• Trademark: SHUODE
• Origin: China
• HS Code: 321410900
• Production Capacity: 150000pieces/Month

Product Description

SHUODE PU FOAM ADHESIVE
This premium one-component aerosol polyurethane adhesive foam cures swiftly upon contact with moisture, delivering rapid and robust adhesion for a variety of construction materials. It is particularly recommended for heat insulation systems.

BASIS CURING	Polyurethane Prepolymer
CURING SYSTEM	Moisture cure
SPECIFIC GRAVITY	213 kg/m3	(ASTM D1622)
TACK-FREE TIME(1 CM WIDTH)	6+2 min	(ASTM C1620)
CUTTING TIME(1CM WIDTH)	20-45min	(ASTM C1620)
CURE-TIME	24 hours
SHEAR STRENGTH	82 kgf/cm²
YIELD VOLUMETRIC	45-55L	(ASTM C1536)
EXPANDING VOLUME	%Max.10
THERMAL CONDUCTIVITY	0,036 W/m.k(at 20C)	(DIN 52612)
COMPRESSION STRENGTH	0,03 MPa(DIN 53421)
WATER ABSORPTION	max.1 vol%
TEMPERATURE RESISTANCE	-40°c to +100°C
APPLICATION TEMPERATURE	0°c to +30°C

 

Application Areas
Ideal for mounting heat insulation panels and filling voids during adhesive application. Also highly effective for bonding wooden construction materials to concrete, metal, etc. Suitable for applications requiring minimal expansion, such as mounting and insulating frames
of windows and doors.

 

SHUODE PU FOAM ADHESIVE
Provides powerful adhesion for polystyrene heat panels (XPS and EPS). Ready for mechanical fastening within two hours. More economical solution, ready to use in an aerosol can. Each can bonds up to 14m² of heat insulation panels. Minimal expansion during drying, with no further expansion or shrinkage after drying.
A lighter material compared to plaster used in heat insulation systems, adding no extra burden or weight to buildings. Performance depends on ambient humidity and temperature conditions.